Sains Malaysiana 44(6)(2015): 905–911

 

Mechanical and Antibacterial Properties of Paper Coated with Chitosan

(Sifat Mekanik dan Antibakteria bagi Kertas yang Disalut dengan Kitosan)

 

 

SARANI ZAKARIA*, CHIN HUA CHIA, WAN HASLINDA WAN AHMAD, HATIKA KACO,

SOON WEI CHOOK & CHI HOONG CHAN

 

School of Applied Physics, Faculty of Science & Technology, Universiti Kebangsaan Malaysia

43600 Bangi, Selangor Darul Ehsan, Malaysia

 

Received: 16 February 2013/Accepted: 6 March 2015

 

ABSTRACT

Recent developments have found the viability of chitosan as a new alternative additive in the pulp and paper technology. This study was carried out to investigate the effect of chitosan as a paper coating which were prepared by dissolution in acetic acid solution. The mechanical properties of coated paper were improved significantly compared with non-coated paper. The FT-IR spectra showed peak evolution at 1558 cm-1 for coated paper due to the existence of amine group. Since FT-IR spectra for the coated paper was almost identical to the chitosan spectrum, it is assumed that there is an obvious physical interaction rather than the chemical interaction. The SEM micrographs showed that some of the chitosan has occupied the pores and some of them adhered only on the surface. This may be due to the chemical similarities between cellulose and chitosan which enhanced the strength of fiber matrixes via hydrogen bonding. The antibacterial property of coated paper showed that chitosan in dried form has no significant effect but effective when applied as wet solution.

 

Keywords: Antibacterial; chitosan; mechanical properties; paper coating

 

ABSTRAK

Perkembangan terkini menunjukkan kesesuaian kitosan sebagai bahan tambah alternatif baru dalam teknologi pulpa dan kertas. Penyelidikan ini mengkaji kesan penyalutan kitosan ke atas kertas yang dilarutkan dalam asid asetik. Sifat mekanik kertas tersalut meningkat dengan ketara berbanding kertas tidak tersalut. Spektrum FT-IR yang diperoleh menunjukkan perbezaan puncak yang jelas antara kertas bersalut dan tanpa salutan pada panjang gelombang 1558 cm-1 yang mengesahkan kehadiran kumpulan amina. Memandangkan spektrum FT-IR yang diperoleh bagi kertas selepas penyalutan menunjukkan profil yang hampir menyerupai spektrum kitosan, maka interaksi yang berlaku diandaikan lebih kepada interaksi fizikal berbanding interaksi kimia. Mikrograf SEM menunjukkan sebahagian daripada kitosan telah mengisi liang-liang pada serabut kertas di samping sebahagiannya lagi berada di bahagian atas permukaan. Ini kerana penyalutan kertas menggunakan kitosan membantu meningkatkan kekuatan ikatan antara serabut dengan serabut pada kertas melalui ikatan hidrogen. Sifat antibakteria kertas tersalut menunjukkan kitosan dalam keadaan kering tiada kesan jelas tetapi efektif apabila dalam larutan basah..

 

Kata kunci: Antibakteria; kitosan; salutan kertas; sifat mekanik

 

REFERENCES

 

Ashori, A., Harun, J., Raverty, W.D., Zin, W.M. & Nor, M. 2005. Effect of chitosan addition on the surface properties of kenaf (Hibiscus cannabinus) paper. Iranian Polymer Journal 14(9): 807-814.

Bordenave, N., Grelier, S. & Coma, V. 2010. Hydrophobization and antimicrobial activity of chitosan and paper-based packaging material. Biomacromolecules 11: 88-96.

Cissé, M., Montet, D., Tapia, M.S., Loiseau, G. & Ducamp- Collin, M.N. 2012. Influence of temperature and relative humidity on the immobilized lactoperoxidase system in a functional chitosan film. Food Hydrocolloids 28(2): 361-366.

Fernandes, S.C.M., Freire, C.S.R., Silvestre, A.J.D., Desbrie`res, J., Gandini, A. & Neto, C.P. 2010. Production of coated papers with improved properties by using a water-soluble chitosan derivative. Industrial and Engineering Chemistry Research 49: 6432-6438.

Fernandes, S., Freire, C.S., Pascoal Neto, C. & Gandini, A. 2008. The bulk oxypropilation of chitin and chitosan and the characterization of the ensuing polyols. Green Chem. 10: 93-97.

Kuusipalo, J., Kaunisto, M., Laine, A. & Kellomaki, M. 2005. Chitosan as a coating additive in paper and paperboard. TAPPI Journal 4(8): 17-21.

Lina, B., Dua, Y., Li, Y., Liang, X., Wang, X., Deng, W., Wang, X., Li, L. & Kennedy, J.F. 2010. The effect of moist heat treatment on the characteristic of starch-based composite materials coating with chitosan. Carbohydrate Polymers 81: 554-559.

Liu, Z., Ge, X., Lu, Y., Dong, S., Zhao, Y. & Zeng, M. 2012. Effects of chitosan molecular weight and degree of deacetylation on the properties of gelatine-based films. Food Hydrocolloids 26(1): 311-317.

Miretzky, P. & Cirelli, A.F. 2009. Hg(II) removal from water by chitosan and chitosan derivatives: A review. Journal of Hazardous Materials 167(1-3): 10-23.

 

 

*Corresponding author; email: szakaria@ukm.edu.my