Sains Malaysiana 45(11)(2016): 1723–1731
Synthesis of Zeolite
from Coal Fly Ash by Hydrothermal Method Without Adding Alumina
and Silica Sources: Effect of Aging Temperature and Time (Sintesis
Zeolit daripada
Abu Cerobong Arang Batu melalui Kaedah
Hidroterma Tanpa
Menambah Sumber Alumina dan Silika: Kesan
Penuaan Suhu
dan Masa) W. CHANSIRIWAT1,2,
D.
TANANGTEERAPONG1
& K. WANTALA1,2,3* 1Department of Chemical Engineering,
Faculty of Engineering, Khon Kaen University, Khon Kaen 40002, Thailand 2Chemical Kinetics and Applied Catalysis
Laboratory (CKCL), Faculty of Engineering, Khon Kaen
University, Khon Kaen
40002, Thailand 3Research Center for Environmental
and, Hazardous Substance Management (EHSM) Faculty of Engineering, Khon Kaen University, Khon Kaen 40002, Thailand Diserahkan: 25 Disember
2015/Diterima: 4 April 2016 ABSTRACT The aim of this research was
to synthesize zeolite from coal fly ash by hydrothermal method.
The effect of aging temperature and time on zeolite P1 synthesis
(Na-P1) from Mae Moh coal fly ash (MFA) without adding any alumina
and silica sources were examined during the synthesized process.
The central composite design (CCD) was used for experimental design
to obtain the optimal process parameters of the aging temperature
(105-195ºC) and time (12-84 h) where the specific surface area
was used as a response. The chemical and physical properties of
Na-P1 such as specific surface area, crystalline phase, compositions
and morphology were examined. The response results showed that
the specific surface area of Na-P1 decreased with an increase
of both aging temperature and time, whereas the XRD intensity
of Na-P1 increased with an increase of both aging temperature
and time. The composition of SiO2/Al2O3 in
mass ratio of coal fly ash was observed, which was suitable to
Na-P1 synthesis. The maximum specific surface area of zeolite
products was found at the designed condition of aging temperature
of 105ºC and time of 12 h. Thus, zeolite P1 can be prepared by
hydrothermal method without adding any alumina and silica sources. Keywords: Coal fly ash; Coal
power plant; response surface methods; zeolite synthesis ABSTRAK Tujuan kajian ini adalah untuk mensintesis
zeolit daripada
abu cerobong arang
batu melalui
kaedah hidroterma. Kesan penuaan suhu
dan masa pada
zeolite sintesis P1 (Na-P1) daripada abu cerobong arang
batu Mae Moh
(MFA)
tanpa menambah
apa-apa sumber alumina dan silika dikaji
semasa proses sintesis.
Pusat reka bentuk
komposit (CCD) telah
digunakan untuk
uji kaji reka
bentuk bagi
mendapatkan parameter proses optimum pada
suhu penuaan
(105-195ºC) dan masa (12-84 h) dengan kawasan permukaan tertentu digunakan sebagai tindak balas. Sifat kimia dan fizikal Na-P1 seperti kawasan permukaan yang khusus, fasa hablur,
komposisi dan
morfologi telah ditentukan. Hasil maklum balas
menunjukkan bahawa kawasan permukaan tertentu Na-P1 menurun dengan peningkatan suhu penuaan dan
masa, manakala keamatan
XRD
Na-P1 terus meningkat
dengan peningkatan suhu penuaan dan
masa. Komposisi oleh SiO2/Al2O3 dalam nisbah jisim
abu cerobong
arang batu diperhatikan,
sesuai untuk
sintesis Na-P1. Kawasan maksimum permukaan tertentu produk zeolit telah ditemui
pada satu
keadaan penuaan suhu 105ºC dan masa 12 h. Oleh itu, zeolit
P1 boleh disediakan
dengan menggunakan kaedah hidroterma tanpa menambah apa-apa sumber alumina dan silika. Kata kunci: Abu cerobong
arang batu;
kaedah gerak balas
permukaan; loji
janakuasa arang batu; sintesis zeolite RUJUKAN Adamczyk, Z.
& Bialecka, B. 2005. Hydrothermal synthesis of zeolites from polish coal fly ash.
Polish Journal of Environmental Studies 14(6): 713-719.
Belviso, C., Giannossa,
L.C., Huertas, F.J., Lettino,
A., Mangone, A. & Fiore, S. 2015.
Synthesis of zeolites at low temperatures in fly ash-kaolinite mixtures.
Microporous and Mesoporous Materials 212: 35-47. Bukhari,
S.S., Behin, J., Kazemian,
H. & Rohani, S. 2015. Conversion
of coal fly ash to zeolite utilizing microwave and ultrasound
energies: A review. Fuel 140: 250-266. Cama, J., Ayora, C., Querol, X. & Ganor, J. 2005. Dissolution
kinetics of synthetic zeolite NaP1 and its implication to zeolite
treatment of contaminated waters. Environmental Science
& Technology 39(13): 4871-4877. Cardoso, A.M., Horn, M.B., Ferret, L.S., Azevedo,
C.M.N. & Pires, M. 2015. Integrated synthesis of zeolites 4A and Na-P1 using coal fly ash for
application in the formulation of detergents and swine wastewater
treatment. Journal of Hazardous Materials 287: 69-77.
Grela, A.,
Hebda, M., Łach,
M. & Mikuła, J. 2016. Thermal
behavior and physical characteristics of synthetic zeolite from
CFB-coal fly ash. Microporous and Mesoporous Materials 220:
155-162. Izidoro, J.C., Fungaro,
D.A., Santos, F.S. & Wang, S. 2012. Characteristics of Brazilian
coal fly ashes and their synthesized zeolites. Fuel Processing
Technology 97: 38-44. Kazemian, H.,
Naghdali, Z., Kashani,
T.G. & Farhadi, F. 2010. Conversion
of high silicon fly ash to Na-P1 zeolite: Alkaline fusion followed
by hydrothermal crystallization. Advanced
Powder Technology 21(3): 279-283. Krasae, N.
& Wantala, K. 2015. Enhanced nitrogen selectivity for nitrate reduction on Cu-nZVI by TiO2 photocatalysts
under UV irradiation. Applied Surface
Science 380: 309-317. Ma, X., Zhang, Z. & Wang, A. 2016. The
transition of fly ash-based geopolymer
gels into ordered structures and the effect on the compressive
strength. Construction and Building Materials 104: 25-33.
Moutsatsou, A.,
Stamatakis, E., Hatzitzotzia,
K. & Protonotarios, V. 2006. The utilization of Ca-Rich and Ca–Si-Rich fly ashes in zeolites production.
Fuel 85(5-6): 657-663. Murayama, N., Yamamoto, H. & Shibata, J. 2002. Mechanism of zeolite synthesis from coal fly ash by alkali hydrothermal
reaction. International Journal of Mineral Processing
64(1): 1-17. Okoye,
F.N., Durgaprasad, J. & Singh, N.B.
2015. Mechanical properties of alkali activated flyash/kaolin
based geopolymer concrete. Construction
and Building Materials 98: 685-691. Onutai, S., Jiemsirilers,
S., Thavorniti, P. & Kobayashi,
T. 2015. Aluminium hydroxide waste based geopolymer
composed of fly ash for sustainable cement materials. Construction
and Building Materials 101: 298-308. Phoo-Ngernkham, T., Sata,
V., Hanjitsuwan, S., Ridtirud,
C., Hatanaka, S. & Chindaprasirt,
P. 2015. High calcium fly ash geopolymer
mortar containing Portland cement for use as repair material.
Construction and Building Materials 98: 482-488. Pimraksa, K.,
Chindaprasirt, P. & Setthaya,
N. 2010. Synthesis of zeolite phases from combustion by-products.
Waste Management and Research 28(12): 1122-1132. Rongsayamanont, C.
& Sopajaree, K. 2007. Modification
of synthetic zeolite pellets from lignite fly ash A: The pelletization. In World of Coal Ash (WOCA).
pp. 1-9. Northern Kentucky, USA. http://www.flyash.info/2007/12rongsay.pdf.
Sang, S., Liu, Z., Tian,
P., Liu, Z., Qu, L. & Zhang, Y. 2006. Synthesis
of small crystals zeolite NaY.
Materials Letters 60(9-10): 1131-1133. Suwannaruang, T., Rivera,
K.K.P., Neramittagapong, A. & Wantala,
K. 2015.
Effects of hydrothermal temperature and time on uncalcined
TiO2 synthesis for reactive Red 120 photocatalytic
degradation. Surface and Coatings Technology 271:
192-200. Thuadaij, P. & Nuntiya, A. 2012. Effect of the SiO2/Al2O3
Ratio on the synthesis of Na-X zeolite from Mae Moh
fly ash. ScienceAsia
38(3): 295-300. Volli, V. & Purkait, M.K. 2015. Selective preparation of zeolite
X and A from flyash and its use as catalyst
for biodiesel production. Journal of Hazardous Materials
297: 101-111. Wei, N., Wang,
X. & Guan, W. 2015.
Synthesis of pure zeolite from coal fly ash
for ammonium removal. Chinese Journal of Environmental
Engineering 9(2): 795-799. Yodsa-nga, A., Millanar, J.M., Neramittagapong,
A., Khemthong, P. & Wantala,
K. 2015.
Effect of manganese oxidative species in as-synthesized K-OMS 2 on
the oxidation of benzene. Surface and Coatings Technology
271: 217-224. Zhang, X., Tang,
D., Zhang, M. & Yang, R. 2013a. Synthesis of NaX zeolite:
Influence of crystallization time, temperature and batch molar
ratio SiO2/Al2O3 on the particulate
properties of zeolite crystals. Powder Technology 235:
322-328. Zhang, Z., Li,
J., Li, H., Wang, H., Zhu, J. & He, Q. 2013b. Dynamic formation of zeolite synthesized
from fly ash by alkaline hydrothermal conversion. Waste Management
and Research 31(11): 1160-1169. *Pengarang untuk surat-menyurat; email: kitirote@kku.ac.th
|
|||
|